文献名称:CP276铝-锂合金的固溶温度研究
    前言:探讨了固溶温度对CP276铝-锂合金显微组织和力学性能的影响。研究证明,提高固溶温度可以促进Cu、Li原子基体溶解,进而提高合金时效的沉淀强化效果.并且发现,该合金经固溶处理后可得到未完全再结晶组织,这种微观组织将对基体产生“组织强化效应”,随着固溶温度升高,合金的再结晶程度也有所增加,从而使组织强化效应受到削弱。力学性能测定结果显示,CP276合金的理想固溶温度为 530℃左右。
    The effect of solid solution treatment (SST) temperature on the microstructure and mechanical properties for aluminium-lithium alloy CP276 was experimentally explored. It is verified that the increasing of SST temperature promoted the dissolving of Cu, Li atoms to solid solution matrix, and hence improved the ageing strengthening effect upon the alloy. It is also found that, incompletely recrystallized structure could be obtained after solid solution treatment, which helpfully providing structure-strengthen...
文献名称 CP276铝-锂合金的固溶温度研究
Article Name
英文(英语)翻译
Study on Solid Solution Treatment Temperature for Al-Li Alloy CP276;
作者 谢绍俊;
Author XIE Shao -jun (Southewest Aluminium Fabrication Plant;Chongqing 401326;China);
作者单位
Author Agencies
西南铝加工厂技术中心;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 铝-锂合金; 固溶处理; 显微组织; 力学性能;
Keywords Al-Li alloys;solid solution treatment;microstructure;mechanical properties;
铝锂合金的研究与发展
铝锂合金自动钨极氩弧焊接工艺研究
1420铝锂合金动态低应力无变形焊接技术
新技术在铝锂合金焊接中的应用
1420铝锂合金激光焊接气孔抑制技术
ML377铝锂合金热稳定性研究
预时效对高强铝锂合金2A97组织和性能的影响
01420铝锂合金的粒子激发再结晶形核
预变形对高强Al-Cu-Li-X铝锂合金组织和性能影响
铝锂合金微弧氧化陶瓷膜层特性的研究

ChemYQ.com ©2005  京ICP备05016959号