文献名称:真空感应熔炼超纯净镍基高温合金脱氮的研究
    前言:研究了真空感应熔炼Ni基高温合金过程中的脱氮行为.计算了不同真空度及加Al和Ti条件下Ni-6Gr-5Go-2Mo-6W合金在1600℃时氮的溶解度.实验表明在CaO坩埚精炼过程中加Al对脱氮有促进作用;加Ti则对脱氮有明显不利影响.提高熔炼真空度是促进脱氮的有力措施
    The denitrogenation behavior during vacuum induction melting (VIM) Ni-base su- peralloy using CaO crucible was studied, and the dissolubilities of nitrogen under different vacuum levels as well as Al and Ti adding amounts at 1600 C were also calculated. The results show that Al addition has evident effect to denitrogenation and Ti addition has adverse effect to denitrogenation. The increase of vacuum level is a powerful way to accelerate the rate of denitrogenation.
文献名称 真空感应熔炼超纯净镍基高温合金脱氮的研究
Article Name
英文(英语)翻译
DENITROGENATION DURING VIM REFINING Ni-BASE SUPERALLOY;
作者 牛建平; 杨克努; 金涛; 孙晓峰; 管恒荣; 胡壮麒;
Author NIU Jianping;YANG Kenu;JIN Tao;SUN Xiaofeng;GUAN Hengrong;HU Zhuangqi Institute of Metal Research;The Chinese Academy of Sciences;Shenyang 110016 Department of Materials Engineering;Shenyang University;Shenyang 110044 Correspondent. NIU Jianping;
作者单位
Author Agencies
中国科学院金属研究所; 中国科学院金属研究所 沈阳 110016沈阳大学材料工程系; 沈阳;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 Ni基高温合金; 真空感应熔炼; CaO坩埚; 脱氮;
Keywords Ni-base superalloy;vacuum induction melting;CaO crucible;denitrogenation;
铸铁CrMo表面激光熔覆Ni基高温合金粉末的磨损特性
新型Ni基高温合金中析出相的热力学模拟计算
Ni基高温合金中有序化和电子结构的计算
Ni_3Al基高温合金瞬态液相扩散连接过程中元素扩散行为研究
定向凝固Ni_3Al基高温合金IC6A的真空钎焊
EBPVD制备ODS Ni基高温合金抗氧化性能研究
激光冲击处理后Ni基高温合金的性能
Ni基高温合金攻丝中高速钢丝锥的摩擦磨损性能研究
高W型Ni基高温合金M963中碳化物研究
Ni基高温合金真空感应熔炼脱硫

ChemYQ.com ©2005  京ICP备05016959号