文献名称:Nd_(60)Fe_(30)Al_(10)大块非晶的制备及其热稳定性
    前言:采用熔渣包覆水淬法获得了直径为 6 mm,长度为 50 mm的非晶 Nd60Fe30Al10合金,并对其非晶形成能力进行了研究.在三元系非晶合金中,除 Pd基合金外,这是目前所报道的采用水淬法所能获得的最大尺寸的非晶合金 对 Nd70Fe20Al10,在同样的条件下可获得直径为 3 mm,长度为 50 mm的部分非晶组织 与普通铜模铸造方法所获得的临界直径相比,前者提高了 2 mm,而后者降低了 4 mm.利用 DTA 和 DSC 对 Nd60Fe30Al10合金的熔点和形成能力进行了分析,所计算的临界冷却速率为0.55K/s,表明该合金具有较大的非晶形成能力.表观晶化能计算结果和 DSC曲线分析表明,Nd60Fe30Al10非晶的热稳定性较低
    Bulk amorphous Nd60Fe30Al10 alloy with a diameter of 6 mm and length of 50 mm was prepared by water quenching the molten alloy together with B2O3 flux medium in an quartz tube. It is 2 mm larger in diameter than that fabricated by the copper mould casting previously. For bulk Nd70Fe20Al10 alloy, however, it contained certain crystalline phase(s) when fabricated into a sample with 3 mm in diameter and 50 mm in length by the same method, being at least 4 mm smaller in diameter than that fabricated by copper m...
文献名称 Nd_(60)Fe_(30)Al_(10)大块非晶的制备及其热稳定性
Article Name
英文(英语)翻译
PREPARATION AND THERMAL STABILITY OF BULK Nd_(60)Fe_(30)Al_(10) AMORPHOUS ALLOY;
作者 邱克强; 王爱民; 张庆生; 张海峰; 丁炳哲; 胡壮麒;
Author QIU Keqiang WANG Aimin;ZHANG QingBheng;ZHANG Hadeng;DING Bingzhe;HU Zhuangqi State Key Laboratory of RSA;Institute of Metal Research;The Chinese Academy of Sciences;Shenyang 110016;Department of Materials;Liaoning Institute of Technology;Jinzhou;
作者单位
Author Agencies
中国科学院金属研究所快速凝固非平衡合金国家重点实验室; 中国科学院金属研究所快速凝固非平衡合金国家;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 Nd60Fe30Al10大块非晶合金; 熔渣包覆水淬法; 非晶形成能力; 热稳定性;
Keywords bulk Nd60Fe30Al10 amorphous alloy;fluxed water quenching method;glass- forming ability;thermal stability;
表面效应对纳米铜杆拉伸性能影响的原子模拟
TiAl基合金高温气体渗氮
Ni-P-金刚石化学复合镀层与钢基的扩散
快速凝固Ni-Al合金中的组成相
超纯净化18Ni(350)马氏体时效钢的研究
NiAl-28Cr-5Mo-1Hf合金的高温氧化行为研究
Ni-Ti合金在650-850℃空气中的氧化行为研究
2024Al与SiC_p/2024Al复合材料的腐蚀与腐蚀控制研究
SiC_p/2024Al复合材料阳极氧化膜耐蚀性的电化学阻抗研究
CREM法半连续铸造Al合金非枝晶组织的形成机制

ChemYQ.com ©2005  京ICP备05016959号