文献名称:Mg_3MNi_2(M=Ti,Al)的晶体结构
    前言:Al和Ti对Mg2Ni结构中部分Mg的取代,得到与Mg2Ni晶体结构不同的新型合金多晶X射线结构分析表明,其化学式为Mg3MNi2(M=Ti,Al),立方晶系,空间群Fd3m, Z=16,48个Mg坐落在48(f),16个 M(M=Al, Ti)坐落在16(d)位,32个Ni坐落在32(e)位,Mg3AlNi2的晶胞参数a=1.15474(2)nm, Mg3TiNi2的a=1.16178(2)nm.与Mg2Ni相比,Mg3MNi2合金的晶体密度更大,Mg-Ni键长更长,吸放氢温度降低,循环寿命延长.
    A new phase different to Mg2Ni was obtained when Mg component in Mg2Ni was partially replaced by Al or Ti. X-ray powder diffraction structure analysis showed that the new phase is of cubic system, S. G. Fd3m (No.227), the chemical formula Mg3MNi2 (M=Al, Ti). Z=16, sixteen molecules per unit cell, cell parameter a=1.15474(2) nm for Mg3AlNi2 and a=l.16178(2) nm for Mg3TiNi2, 48 atoms of Mg are located on 48(f) sites, 16 atoms of M (Ti, Al) on 16(d) and 32 atoms of Ni on 32(e). Compared with Mg2Ni, Mg3AlNi2 ha...
文献名称 Mg_3MNi_2(M=Ti,Al)的晶体结构
Article Name
英文(英语)翻译
THE CRTSTAL STRUCTURE OF NEW HYDROGEN STORAGE Mg_3MNi_2 (M=Al, Ti) ALLOYS;
作者 吕光烈; 陈林深; 胡秀荣; 王连邦; 袁华堂;
Author LU Guanglie;CHEN Linshen;HU Xiurong Center Laboratory;Zhejiang University;Hangzhou 310028 WANG Lianbang;YUAN Huantang Institute of New Energy Material Chemistry;Nankai University;Tianjin 300071;
作者单位
Author Agencies
浙江大学中心实验室; 南开大学新能源材料化学所;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 贮氢合金; XRD结构分析; Mg2MNi2(M=Al; Ti);
Keywords hydrogen storage alloys;XRD structure analysis;Mg2MNi2(M=Al;Ti);
AB_5型低钴含铁贮氢合金电极材料的研究进展
Al替代Mg对La_2MgNi_(7.5)Co_(1.5)贮氢合金电化学循环稳定性的影响
Al替代Mg对La_2MgNi_(7.5)Al_(1.5)贮氢合金相结构和电化学性能的影响(英文)
镍氢电池复合贮氢合金负极材料的研究进展
电解液中添加Cu(OH)_2对La_2MgNi_(7.5)Co_(1.5)贮氢合金电极电化学性能的影响
退火对La_(0.75)Mg_(0.25)Ni_(3.5)Co_(0.4)贮氢合金电化学性能的影响
Mg-Ni基贮氢合金元素取代改性研究进展
Ti_(0.8)Zr_(0.2)V_(1.1)Mn_(0.9-x)Ni_(0.4)Cr_x固溶体贮氢合金结构和电化学性能
Mg-Ni系贮氢合金的改性
快淬La-Mg-Ni系贮氢合金的电化学性能及微观结构

ChemYQ.com ©2005  京ICP备05016959号