文献名称:纳米氧化锌粉的表面改性研究
    前言:以Zn(NO3)2·6H2O和CO(NH2)2为原料,采用均相沉淀法制备纳米氧化锌粉.用扫描电镜对产物粒度大小、形貌进行观察,并对其影响因素进行了探讨.结果表明,在反应温度为120℃,反应时间为2.5h时,所制的纳米氧化锌的产率最大.用不同的表面改性剂对纳米ZnO进行表面改性,粉体不再发生团聚.图6,表7,参5.
    Using Zn(NO3)26H2O and CO(NH2)2 as raw materials,nanoZnO particles were prepared by using a homogeneous precipitation method. Size and morphology of nanoZnO powders were investigated by means of SEM, and the factors effecting their properties were discussed. The results indicated the efficiency of production reached the maximum at temperature 120 ℃ for 2.5 h. The nanoZnO powders were modified by different surface active agents, so that the particles were not agglomerated.6figs.,7tabs.,5refs.
文献名称 纳米氧化锌粉的表面改性研究
Article Name
英文(英语)翻译
Study on surface modification of nano-ZnO powders;
作者 葛岭梅; 贾鹏涛; 薛韩玲; 许满贵;
Author GE Lingmei;JIA Pengtao;XUE Hanling;XU Mangui(Xi'an University of Science and Technology;Xi'an 710054;China);
作者单位
Author Agencies
西安科技学院材料系; 西安科技学院材料系 陕西西安710054; 陕西西安710054; 陕西西安;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 均相沉淀法; 纳米氧化锌; 改性; 团聚; 过饱和;
Keywords homogeneous precipitation;nano-ZnO;modification;agglomeration;supersaturation;
微波均相沉淀法制备Ce:(Y,Gd)_3Al_5O_(12)荧光粉
配合-均相沉淀法制备纳米掺锑氧化锡
均相沉淀法制备NiO纳米粒子及磁性研究
微波均相沉淀法制备YAG透明陶瓷
微波均相沉淀法制备Nd:YAG纳米粉体及其表征
均相沉淀法制备Nd∶YAG透明激光陶瓷材料研究
均相沉淀法制备铟锡氧化物纳米材料的研究
均相沉淀法制备AACHH阻燃晶须及其生长机理研究
草酸二甲酯均相沉淀法制备超细CeO_2的研究
表面活性剂对均相沉淀法制备单晶Ce_2O(CO_3)_2·H_2O微粉形貌及形成机理的影响(英文)

ChemYQ.com ©2005  京ICP备05016959号