文献名称:膜相渗透原位化学聚合法制备PAn/CA复合透膜
    前言:采用膜相渗透原位化学聚合法 ,使苯胺 ( An)原位化学聚合于醋酸纤维素 ( CA)基体膜的微孔壁中 ,得到均匀分布的 PAn/CA复合导电透膜 .通过研究聚合反应条件对复合透膜的导电性能和 CO2 /O2 表观分离性能的影响 ,获得了制备性能较优的 PAn/CA复合导电透膜的适宜条件 .结果表明 ,采用膜相渗透化学原位聚合法制备的 PAn/CA复合导电透膜 ,平均孔径明显变小 ,孔径分布变窄 ,具有优于 CA基体膜的微孔结构形态 .
    The preparation of PAn/CA composite conductive membrane by in-situ permeating chemical polymerization was introduced in this paper. By this method, polyaniline was synthesized onto the pore wall of the CA microporous membrane. The influence of preparing conditions on the conductivity and apparent selectivity of CO 2/O 2 was investigated. The pore size and distribution of the resulting membrane were evaluated by the method based on bubble pressure and liquid permeation. SEM, FTIR were employed to character...
文献名称 膜相渗透原位化学聚合法制备PAn/CA复合透膜
Article Name
英文(英语)翻译
Synthesis of PAn/CA Composite Membrane by in-situ Permeating Ploymerization;
作者 杜军; 郑婵娟; 陶长元;
Author DU Jun;ZHENG Chan-Juan;TAO Chang-Yuan * (College of Chemistry and Chemical Engineering;Chongqing University;Chongqing 400044;China);
作者单位
Author Agencies
重庆大学化学化工学院; 重庆大学化学化工学院 重庆;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 导电聚合物; 复合透膜; 膜相渗透原位化学聚合;
Keywords Conductive polymer;Composite membranes;In-situ permeating polymerization;
荧光导电聚合物α,β_i-SiW_(11)M/聚苯胺的固相合成及性质研究
导电聚合物/磁性纳米复合材料:聚苯胺/Fe_3O_4的制备与表征
导电聚合物电磁屏蔽材料及其应用
荧光导电聚合物β_1-SiW_(11)M/聚苯胺的固相合成及性质
纳米结构导电聚合物材料研究进展
导电聚合物超薄膜的制备及性能表征
导电聚合物与磁性粒子复合吸波材料的研究进展
导电聚合物/无机纳米复合材料的研究进展
PEDOT-PSS导电聚合物LB薄膜的制备和性能
PEDT导电聚合物气敏特性研究

ChemYQ.com ©2005  京ICP备05016959号