文献名称:预吸附微波合成纳米NaY沸石晶种制备NaY型分子筛膜
    前言:在常压回流的微波加热体系中成功地合成出纳米尺寸的 Na Y分子筛 ,XRD和 SEM等表征结果表明 ,分子筛具有 40 nm左右的平均晶粒尺寸 .以其为晶种 ,预吸附在多孔氧化铝载体上 ,结合原位水热法进行二次晶化 ,制备出较为致密的 Na Y分子筛膜 ,该膜主要以孪生聚晶的形式存在 .CO2 /N2 气体分离测试结果显示 ,随着温度的升高 ,分子筛膜的气体分离能力呈上升趋势 ,在 1 40℃时真实选择分离系数达到最大值4.0 .
    Nanosized NaY zeolite was successfully synthesized by microwave heating at an ambient pressure and under reflux. The XRD and SEM results indicate that the resulted NaY zeolite has an average crystal size of 40 nm. The compact NaY zeolite membranes consisting of twinborn and polycrystalline crystal were synthesized on a porous alumina substrate by using pre-absorbed nanosized NaY zeolite obtained above and then by being combined with a secondary in situ synthesis. The measuring result for the separation of C...
文献名称 预吸附微波合成纳米NaY沸石晶种制备NaY型分子筛膜
Article Name
英文(英语)翻译
NaY Zeolite Membrane Prepared by Using Pre-absorbed Nanosized NaY Zeolite Synthesized by Microwave Heating;
作者 程志林; 林海强; 晁自胜; 万惠霖;
Author CHENG Zhi-Lin 1;2*;LIN Hai-Qiang 2;CHAO Zi-Sheng 2;WAN Hui-Lin 2 (1. Department of Chemistry;East Normal University;Shanghai 200062;China;2. State Key Laboratory for Physical Chemistry of Solid Surface;Department of Chemistry;Xiamen University;Xiamen 361005;China);
作者单位
Author Agencies
华东师范大学化学系; 厦门大学化学系; 固体表面物理化学国家重点实验室; 固体表面物理化学国家重点实验室 上海;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 微波加热; 纳米; NaY分子筛膜; 分离;
Keywords Microwave heating;Nanometer;NaY Zeolite membrane;Separation;
微波加热及其在酒类催熟杀菌中的应用
微波加热制备低水硼酸锌
微波加热含碳碳酸锰矿粉升温特性研究
微波加热白云石生产煅白的反应机理
微波加热碳酸钾法制备烟杆基高比表面积活性炭
蒸煮与微波加热对牛肉肌内脂肪中脂肪酸组成的影响
含碳铬矿粉微波加热体还原显微矿相结构的研究
砂岩储集层微波加热产生微裂缝的机理及意义
炭黑填充HDPE的力学性能和微波加热性能
纳米晶型MnCo_2O_4的微波加热法制备及其电催化性能

ChemYQ.com ©2005  京ICP备05016959号