文献名称:加捻参数对转杯纺棉氨复合纱性能的影响
    前言:选用44.4dtex和77.8dtex两种规格的氨纶长丝在经过改造的转杯纺纱机上纺制棉氨复合纱,设计了5种成纱捻度,测试分析了设计捻度对转杯纺棉氨复合纱结构和性能的影响情况。结果表明,在相同捻系数条件下棉氨复合纱较纯棉转杯纱条干均匀,表面光洁,断裂强力断裂伸长率也较大;随着捻系数的增加,棉氨复合纱断裂强力的变化趋势是先增大后减小,断裂伸长率则呈增大趋势,但加捻效率下降。
    Spinning cotton polyurethane complex yarn in reformed rotor spinning machine with 44.4 dtex and 77.8 dtex polyurethane filaments, five twist is designed, and influence on structure and performance of cotton polyurethane complex yarn of design twist is tested. The test shows —— in the condition of same twist factor, cotton polyurethane complex yarn has better evenness than cotton rotor yarn, and has better surface finish, and high break strength & elongation at break which are increasing with twist factor. C...
文献名称 加捻参数对转杯纺棉氨复合纱性能的影响
Article Name
英文(英语)翻译
Influence of Twisting Parameters on Performance of Cotton Polyurethane Complex Rotor Yarn;
作者 张海霞; 薛元; 王善元;
Author Zhang Haixia1 Xue Yuan2 Wang Shanyuan1 (1 Donghua University;2 Jiaxing College);
作者单位
Author Agencies
东华大学; 嘉兴学院;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 转杯纺; 棉氨复合纱; 捻系数; 加捻效率; 条干均匀度; 强力; 毛羽;
Keywords Rotor Spinning;Cotton Polyurethane Complex Yarn;Twist Factor;Twisting Efficiency;Evenness;Strength;Hairiness;
转杯纺重定量工艺优化
转杯纺复合纱中长丝组分比的研究
转杯纺关键部件与成纱质量的探讨
转杯纺三项工艺参数的优化组合对C32tex纱质量影响的研究
转杯纺假捻盘的应用
合理配棉提高转杯纺纱质量
转杯纺与赛络纺氨纶/棉包芯纱的性能对比
转杯纺纺制针织纱工艺研究(上)
涤棉转杯纺起绒纱的生产研究
转杯纺工艺优选及质量控制

ChemYQ.com ©2005  京ICP备05016959号