文献名称:T225NG钛合金氢脆行为的研究
    前言:通过渗氢试样的常温力学性能试验和双悬臂梁试样在高温高压高纯水中的腐蚀试验来研究T225NG钛合金氢脆行为。研究结果表明:T225NG钛合金在空气和高温高压高纯水的环境下具有良好的抗氢脆性能; T225NG 钛合金的氢脆属于氢化物脆性,这是由于T225NG钛合金中渗入的氢导致氢化物的析出引起的;T225NG钛合金表面氧化膜对它优良的抗氢脆性能起了决定性的作用。
    Through the tests of mechanical properties of charging hydrogen and the corrosion tests in loop water of high temperature and high pressure, hydrogen brittleness of T225NG Ti-alloy was studied. The results show that T225NG Ti-alloy has good property of resisting hydrogen brittleness in atmosphere and in loop water. Hydrogen brittleness of T225NG Ti-alloy is hydride brittleness. This is due to the forming of hydride caused by a large amount of hydrogen dissolved in and oxide film on the surface of T225NG ...
文献名称 T225NG钛合金氢脆行为的研究
Article Name
英文(英语)翻译
Research on Hydrogen Brittleness of T225NG Ti-alloy;
作者 徐济进; 严铿; 朱政强; 陈立功;
Author Xu Jijin 1 Yan Keng 2 Zhu Zhengqiang 1 Chen Ligong 1 1.Shanghai Jiaotong University;Shanghai;200030 2.East China Shipbuilding Institute;Zhenjiang;212003;
作者单位
Author Agencies
上海交通大学; 华东船舶工业学院; 上海交通大学 上海; 200030; 212003;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 钛合金; 氢脆; 氢化物; 表面氧化膜;
Keywords Ti-alloy;hydrogen brittleness;hydride;oxide film of surface;
PCBN刀具高速切削钛合金切削性能研究
BT20钛合金表面渗氧研究
原子吸收光谱法测定TG6钛合金中痕量镍不确定度的分析
钛合金熔模精密铸造用氮化硼基复合型壳的探索试验
不锈钢和钛合金攻丝方法研究
TC4钛合金与0Cr18Ni10Ti不锈钢真空热轧连接
处理频率对TC4钛合金微弧氧化膜特性的影响
TA15钛合金疲劳寿命反推研究
TC11钛合金在人造海水中的腐蚀磨损特性研究
板状钛合金拉伸试件的设计及其制造

ChemYQ.com ©2005  京ICP备05016959号