文献名称:AAO模板上碳纳米棒定向膜的制备及摩擦性能分析
    前言:在多孔阳极氧化铝(AAO)模板上的有序纳米孔中电化学沉积过渡金属Co作为催化剂,通过催化化学气相沉积(CCVD)法制备出有序、均匀的非晶态碳纳米棒定向膜.采用扫描电子显微镜(SEM)、能谱仪(EDS)及激光Raman光谱等方法分析了非晶态碳纳米棒定向膜的微观结构和形貌,并讨论了其摩擦因数与载荷及速度的关系.实验结果表明,非晶态碳纳米棒定向膜具有较小的摩擦因数,并且随着载荷的增加而减小,随速度的增加而先减小后增大,当滑动速度为0.18m/s时摩擦因数最小.
    A transition metal Co as catalyst was electrodeposited in the ordered nanosized pores of anodic aluminum oxide (AAO) template, and the aligned film of amorphous carbon nanorods was obtained by catalytic chemical vapor deposition. The microstructures and morphology of the aligned film were investigated by scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDS) and laser Raman spectroscopy. The friction properties were performed at different load and velocity. The aligned film of amorph...
文献名称 AAO模板上碳纳米棒定向膜的制备及摩擦性能分析
Article Name
英文(英语)翻译
Preparation and friction properties of aligned membrane of amorphous carbon nanorods on AAO template;
作者 江春喜; 涂江平; 郭绍仪; 扶名福; 赵新兵;
Author JIANG Chun-xi 1;2;TU Jiang-ping2;GUO Shao-yi3;FU Ming-fu1;ZHAO Xin-bing2 (1.College of Mechanical Electronic and Engineering;Nanchang University;Nanchang 330029;China;2.Department of Materials Science and Engineering;Zhejiang University;Hangzhou 310027;3.Department of Mechanical Engineering;Zhejiang Sci-Tech University;Hangzhou 310012;China );
作者单位
Author Agencies
南昌大学机电工程学院; 浙江大学材料科学与工程学系; 浙江理工大学机械工程学系; 浙江大学材料科学与工程学系 江西南昌330029浙江大学材料科学与工程学系; 浙江杭州; 江西南昌;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 阳极氧化铝模板; 碳纳米棒; 定向膜; 摩擦因数;
Keywords anodic aluminum oxide (AAO) template;carbon nanorod;aligned membrane;friction coefficient;
阳极氧化铝模板有序度影响因素的研究
制备工艺对多孔阳极氧化铝模板的影响
阳极氧化铝模板中直接直流电沉积铁纳米线
高孔密度阳极氧化铝模板的制备及结构表征
基于阳极氧化铝模板的金属纳米孔阵列膜制备
高度有序多孔阳极氧化铝模板的制备
纳米多孔阳极氧化铝模板制备的研究
多孔阳极氧化铝模板制备金属/合金纳米管的研究进展
阳极氧化铝模板制备过程的分析和应用
阳极氧化铝模板法制备CoPt纳米管

ChemYQ.com ©2005  京ICP备05016959号