文献名称:铝合金阳极氧化膜干燥方式对其粘接性能的影响
    前言:利用拉剪实验及楔子实验等测定2A14铝合金粘接件的结合强度和耐久性,结合扫描电镜及红外分析等方法,研究铝合金粘接前阳极氧化膜的微观结构及含水量对其粘接性能的影响。结果表明:铝合金磷酸阳极氧化膜经过冷风吹干、50℃烘干和100℃烘干处理后,粘接试样的拉剪强度随烘干温度升高略有增加;粘接试样的湿热耐久性以50℃烘干处理后的稍好,而100℃烘干处理后,由于氧化膜中产生大量微裂纹,使其耐久性有所下降;氧化膜经过沸水封闭处理后,由于膜中含水量很大及封孔处理限制粘合剂渗透,导致其拉剪强度和湿热耐久性皆明显降低。
    The aluminum alloy samples were anodized in the phosphoric acid solutions,the microstructure and topography of the anodic films were examined using SEM and AFM,and their adhesive properties were studied by the lap-shear test and wedge test.Prior to bonding,the PAA films were dried in cool wind,at 50℃,at 100℃,or sealed in boiling water.The results showed that the adhesive bonding strength of the alloy were slightly improved with the increase of drying temperature;the durability of bonding alloys by dried at ...
文献名称 铝合金阳极氧化膜干燥方式对其粘接性能的影响
Article Name
英文(英语)翻译
Effects of drying methods of anodic films on adhesion properties of aluminum alloy;
作者 张晓丰; 赵蕊; 张金生; 赵旭辉; 左禹;
Author Zhang Xiaofeng1 Zhao Rui1 Zhang Jinsheng2 Zhao Xuhui1 Zuo Yu1(1.School of Materials Science and Engineering;Beijing University of Chemical Technology;Beijing 100029;2.Department of Chemical Engineering;Wuhan University of Science and Engineering;Wuhan 430073);
作者单位
Author Agencies
北京化工大学材料科学与工程学院; 武汉科技学院化工系; 北京化工大学材料科学与工程学院 北京;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 铝合金; 阳极氧化; 粘接; 干燥;
Keywords aluminum alloy;anodizing;adhesion;deoxidizing;
喷射沉积高镁铝合金沉积态微观组织特征
轧制铝合金叠层板变形量与结合强度的关系初探
LC4铝合金阳极氧化膜的电参数特性与封孔性能研究
7B04铝合金双级时效的微观组织与性能
LY12CZ铝合金随焊锤击碾压工艺优化
影响铝合金轮毂电镀层内应力的工艺研究
铝及铝合金用钎剂的发展现状和趋势
2124铝合金超厚板断裂韧性的研究
梯度孔径通孔多孔铝合金的空气吸声性能
2519铝合金管材热挤压过程的数值模拟

ChemYQ.com ©2005  京ICP备05016959号