文献名称:复合材料层板损伤失效分析
    前言:基于连续损伤理论,利用多标量损伤模型,考虑单层板失效前由微裂纹损伤所造成的刚度下降,将Hoffman准则作为复合材料单层板在复杂应力状态下的极限损伤条件,应用该准则对含圆孔复合材料层合板在单向拉伸载荷下的损伤破坏过程进行了数值分析,并与常规(无损伤)失效准则的结果进行了比较.计算表明:损伤引起单层刚度下降,使应力重新分布,加速应力向未损伤层和周围单元转移,从而使应力集中得到缓解,层板的单层破坏载荷明显提高,从而提高层板的极限载荷,提高程度受铺层方式的影响.可见,由损伤引起的刚度下降应在层板失效分析中加以考虑.
    Based on progressive damage theory,a non-linear and multi-scale damage model is developed to consider the stiffness reduction caused by micro-crack before the failure of a single lamina.The Hoffman criterion is taken as an ultimate condition for the damage to a single lamina of composite laminate in complex stress state.Then,the criterion is introduced to a numerical analysis made for the damaging failure process of a composite laminate with a hole under unilateral load,and the result of the analysis is com...
文献名称 复合材料层板损伤失效分析
Article Name
英文(英语)翻译
Analysis of Damaging Failure of Composite Laminates;
作者 刘军; 李英梅; 黄宝宗;
Author LIU Jun;LI Ying-mei;HUANG Bao-zong(School of Sciences;Northeastern University;Shenyang 110004;China.);
作者单位
Author Agencies
东北大学理学院; 东北大学理学院 辽宁沈阳; 辽宁沈阳;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 复合材料层板; 损伤失效准则; 多标量损伤; 逐步损伤;
Keywords composite laminate;damage failure criterion;multi-scale damage;progressive damage;
复合材料层板精化理论两类推导方法的一致性
正交复合材料层板的微损伤建模研究
基于复合材料层板稳定性的铺层参数优化设计方法
复合材料层板低速冲击后剩余压缩强度
损伤复合材料层板胶接修理的优化设计
环氧复合材料层板热压成型孔隙缺陷影响因素
缝合复合材料层板面内局部纤维弯曲模型及刚度预报
复合材料层板热压工艺参数的分析与优化
带有铝板复合材料层板固化过程中残余应力演化
复合材料层板静压入破坏机制