文献名称:厚膜型La_2CuO_4的氧敏性能
    前言:采用甘氨酸-硝酸盐法合成了La2CuO4复合氧化物,并制成厚膜型氧敏元件。结果表明,在400~700℃之间,厚膜型La2CuO4的灵敏度随着测试温度的升高而逐渐降低。La2CuO4气敏元件的灵敏度(RN2/RO2)主要由表面载流子浓度决定,随着测试温度的升高,吸附氧在粒子表面的脱附速率增大,导致空穴载流子浓度随温度的升高而降低,从而使灵敏度下降。厚膜型La2CuO4在400℃时的灵敏度最大,可以达到29.6,远大于烧结型La2CuO4的灵敏度,且厚膜型La2CuO4在400℃对于氧分压变化具有快速的响应,响应时间约为4 s。
    Perovskite-type oxide La2CuO4 was synthesized by the glycine-nitrate process(GNP).The thick film type oxygen-sensing element was fabricated and its oxygen-sensing properties were investigated.The sensitivity of the thick-film La2CuO4 decreased with the increase of the measurement temperature because the oxygen-sensing properties of La2CuO4 was mainly determined by the surface carrier concentration.Oxygen adsorbed on the surface of the La2CuO4 thick films desorbed rapidly with the increase of the measurement...
文献名称 厚膜型La_2CuO_4的氧敏性能
Article Name
英文(英语)翻译
Oxygen-Sensing Properties of La_2CuO_4 Thick Film;
作者 赵伟杰; 赵辉; 霍丽华; 高山;
Author ZHAO Wei-Jie;ZHAO Hui;HUO Li-hua;GAO Shan(Laboratory of Functional Materials;School of Chemistry and Materials Science;HeilongJiang University;Harbin 150080);
作者单位
Author Agencies
黑龙江大学化学化工与材料学院; 黑龙江大学化学化工与材料学院 功能材料省高校重点实验室哈尔滨; 功能材料省高校重点实验室哈尔滨;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 La2CuO4; 厚膜; 氧敏性;
Keywords La2CuO4;thick film;oxygen-sensing property;
通过柠檬酸改性提高载银活性炭的抗菌性能
纳米氧化铁的制备及其对砷的吸附作用
SPE水电解进行H/D同位素分离
二氯化-N,N-′-二(3-脱氢松香酰氧-2-羟丙基)四甲基乙二胺的合成与性能
MgO海/泡石复合载体负载Cu催化剂催化环己醇脱氢
不同提取方法所得褐藻糖胶的理化性质比较
金属锌促进羰基化合物水相嚬呐偶合反应
热致液晶聚酰胺的溶解性能和热性能
糠偶姻单酯类化合物的合成
钙镁硅酸盐溶度积常数的测定

ChemYQ.com ©2005  京ICP备05016959号