文献名称:ZrO_2陶瓷微球成型工艺的研究
    前言:研究了用于ZrO2陶瓷微球成型的方法——内胶凝工艺,系统探讨了工艺温度、原材料浓度以及干燥煅烧条件对工艺及微球形貌的影响。确定了ZrO2陶瓷微球成型的最佳工艺参数,氧氯化锆原料的浓度为1.6mol/L,固化剂六次甲基四胺尿素金属离子摩尔比值为0.68与0.57;成型温度控制在90℃。通过添加稳定剂Y2O3,微球具有TZP材料的结构特征。
    A process of internal gelation for preparing stabilized zirconia ceramic microspheres was developed.The influences of process parameters such as process temperatures,raw material concentrations,and the conditions of drying and calcining on the process and characteristics of the microspheres were investigated in this paper.The experimental results showed that,the optimum concentration of ZrOCl2·8H2O was 1.6mol/L.The optimum ratios of HMTA to metal ions and urea to metal ions were 0.68 and 0.57.And molding te...
文献名称 ZrO_2陶瓷微球成型工艺的研究
Article Name
英文(英语)翻译
Study on the Molding Process of ZrO_2 Ceramic Microspheres;
作者 朱洪龙;
Author ZHU Hong-long (Dean's Office;Zaozhuang University;Zaozhuang;Shandong 277160;China);
作者单位
Author Agencies
枣庄学院教务处 山东枣庄;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 二氧化锆; 陶瓷微球; 成型; 内胶凝工艺;
Keywords Zirconia;Ceramic microspheres;molding;Internal gelation process;
注凝成型超细二氧化锆悬浮体的制备
二氧化锆的相稳定及其制备方法
电解均匀沉淀法制备纳米二氧化锆粉体及其机理
水热法合成羟磷灰石及其包覆二氧化锆粉体的制备
二氧化锆的稳定化及其应用
二氧化锆合成宝石产业现状和发展
静电纺丝法制备硫酸化的二氧化锆/二氧化硅复合纤维
纳米二氧化锆研究进展——Ⅰ性质
纳米二氧化锆研究进展——Ⅱ制备
超细二氧化锆注凝成形料浆流变性研究

ChemYQ.com ©2005  京ICP备05016959号