文献名称:聚氨酯/聚丙烯腈扭曲螺旋纳米纤维的电纺制备
    前言:静电纺丝法对聚氨酯在不同质量分数(4%~16%)和不同电压(14 kV~26 kV)下的可纺性进行了研究;制备了聚氨酯/聚丙烯腈共混溶液扭曲螺旋纤维,研究了聚氨酯和聚丙烯腈不同质量比以及电压对扭曲螺旋纤维形貌的影响.研究结果表明:聚氨酯的质量分数为13%、电压为20 kV时得到的纤维形貌最好;聚氨酯和聚丙烯腈质量比在1∶1~13∶5之间均可得到扭曲螺旋结构的纳米纤维;随着聚氨酯和聚丙烯腈质量比的增加,所得螺旋纤维螺旋环的螺距增大,螺旋环的直径变小;当电压增大时,扭曲螺旋环的螺距减小,螺旋环的直径变大.
    In this paper,spinnability of Polyurethane(PU) with different concentration,which changed from 4% to 16% by weight and varied from 14 kV to 26 kV by voltage,was studied.Then polymeric fibers with curled or helical structures was prepared from solution of PU and polyacrylonitrile(PAN) in N,N-dimethyl-formamide(DMF) by electrospinning.The influence of ratio of PU and PAN and the voltage on the appearance of fibers was also studied.Results showed that the morphology of fibers was the best when PU concentration...
文献名称 聚氨酯/聚丙烯腈扭曲螺旋纳米纤维的电纺制备
Article Name
英文(英语)翻译
Preparation of Curled or Helical PU/PAN Fibers by Electrospinning;
作者 常敏; 李从举;
Author CHANG Min1;LI Cong-ju2(1.School of Materials Science and Engineering;Beijing Institute of Clothing Technology;Beijing 100029;China;2.Beijing Key Laboratory of Clothing Materials R&D and Assessment;China);
作者单位
Author Agencies
北京服装学院材料科学与工程学院; 北京市服装材料研究开发与评价重点实验室 北京;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 静电纺丝; 聚氨酯; 聚丙烯腈; 螺旋纤维;
Keywords electrospinning;PU;PAN;helical fiber;
基于近场静电纺丝的微/纳米结构直写技术
超声波振动在静电纺丝技术中的应用
高压静电纺丝法制备离子液体/聚合物电解质
稀乙酸对聚乙烯醇水溶液静电纺丝性能的影响
环氧树脂的静电纺丝
静电纺丝法制备纳米纤维的研究进展
静电纺丝法制备ZnO纳米纤维及其光催化性能的研究
仿生制备的再生丝素蛋白水溶液的静电纺丝(Ⅰ)——工艺参数及结构特性
利用静电纺丝技术制备新型生物防护材料
静电纺丝法制备Eu~(3+)掺杂的氧化钆纳米纤维

ChemYQ.com ©2005  京ICP备05016959号