文献名称:CVI法制备SiC_p/SiC复合材料的力学性能研究
    前言:对用CVI法制备的SiCp/SiC复合材料的力学性能进行研究。研究表明:材料表现出脆性断裂的破坏失效特征;SiCp/SiC复合材料内部颗粒间、团聚体之间残留的微孔和孔隙等薄弱环节使材料的强度降低;复合材料基体增强相之间有一层由树脂热解而产生的玻璃碳,造成界面的弱结合,使材料强度不高。
    The mechanical properties of SiCp/SiC composite prepared by chemical vapor infiltration (CVI) were studied. Two kinds of pores were found in the preform: pores about several micrometers among the particles and pores about several millimeters among the conglomerations. The pores reduced the strength of composite. The interphase of glass state carbon appeared between the matrix and reinforced phase, which resulted in weak joint.
文献名称 CVI法制备SiC_p/SiC复合材料的力学性能研究
Article Name
英文(英语)翻译
Mechanical properties of SiC_p/SiC composite manufactured by CVI;
作者 汤精明; 王小明;
Author TANG Jing-ming1;2;WANG Xiao-ming2 (1.Anhui University of Technology and Science;Wuhu 241000;China;2.Northwestern Polytechnical University;Xi’an 710072;China);
作者单位
Author Agencies
安徽工程科技学院机械工程系; 西北工业大学材料学院 安徽芜湖241000西北工业大学材料学院; 陕西西安;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 化学气相渗透; SiCp/SiC复合材料; 力学性能; 弯曲强度; 界面;
Keywords chemical vapor infiltration;SiCp/SiC composite;mechanical properties;bending strength;interphase;
镍对C/SiC化学气相渗透碳的催化研究
低压化学气相渗透法制备2.5维SiC_f/SiC复合材料(英文)
低温化学气相渗透法制备C_f/TaC复合材料的研究
化学气相渗透工艺制备C/C研究进展
等温化学气相渗透制备碳化硅复合材料的工艺研究
催化化学气相渗透法制备C/C复合材料
化学气相渗透2.5维C/SiC复合材料的拉伸性能
化学气相渗透碳/碳复合材料热解碳光性特征——热解碳十字消光机理探讨
化学气相渗透法制备三维针刺C/SiC复合材料的烧蚀性能
CH_4化学气相渗透沉积提高焦炭热性质研究

ChemYQ.com ©2005  京ICP备05016959号