文献名称:熔体过热处理对Al-4.7%Cu合金定向凝固力学性能及晶体取向的影响
    前言:在熔体过热温度Ts分别为750、850、950、1050℃时,研究熔体过热温度对Al-4.7%Cu合金定向凝固组织及力学性能的影响,利用综合热分析仪测定Al-4.7%Cu合金熔体结构特征及变化过程,用扫描电镜观察断口形貌。结果表明,定向凝固试样力学性能与非定向凝固的相比,强度提高60%,断后伸长率提高近1倍。断口形貌观察表明,富Cu相明显减少,韧窝数量显著增加。随熔体过热温度提高及过热时间延长,试样强度及塑性提高,随低温保持时间延长,试样强度及塑性变差。Al-4.7%Cu合金枝晶沿择优方向<100>生长,且随熔体过热温度提高,(100)晶面衍射强度减弱,表明晶面取向产生分支。Al-4.7%Cu合金过热处理会使熔体结构(即团簇结构)发生一定变化。
    With the temperature of 750 ℃, 850 ℃, 950 ℃ and 1 050 ℃, the influence of melt superheat temperature Ts on the solidification microstructure and mechanical performance of directionally solidified Al-4.7%Cu alloy was studied. The characteristics of the melt were measured by universal thermo-analyzer. And the fracture morphology was analyzed by SEM. The results show that the mechanical property of directionally solidified sample was much better, the strength is increased by 60% and the elongation can be doubl...
文献名称 熔体过热处理对Al-4.7%Cu合金定向凝固力学性能及晶体取向的影响
Article Name
英文(英语)翻译
Influence of Melt Superheating Treatment on the Mechanical Property and Crystal Orientation of Directionally Solidified Al-4.7%Cu Alloy;
作者 司乃潮; 孙克庆;
Author SI Nai-chao;SUN Ke-qing (School of Materials Science and Engineering;Jiangsu University;Zhenjiang 212013;Jiangsu;China);
作者单位
Author Agencies
江苏大学材料科学与工程学院; 江苏大学材料科学与工程学院 江苏镇江; 江苏镇江;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 过热处理; 定向凝固; 凝固组织; 力学性能; 断口形貌;
Keywords superheat treatment;directional solidification;solidification microstructure;mechanical property;fracture morphology;
熔体过热处理对K465合金晶粒和碳化物的影响
熔体过热处理对Cu基块状非晶形成能力的影响及块状非晶的DSC研究
熔体过热处理对Al-4.7%Cu合金定向凝固组织的影响
熔体过热处理对过共晶Al-Si合金凝固组织的影响
合金熔体过热处理的研究进展
熔体过热处理对定向凝固界面形态及稳定性的影响
熔体过热处理对M963合金凝固偏析的影响
熔体过热处理对M963合金组织和高温持久性能的影响
熔体过热处理对铸造镍基高温合金吸氮行为的影响
合金熔体过热处理研究的国内发展状况

ChemYQ.com ©2005  京ICP备05016959号