文献名称:平衡相对8090Al-Li合金力学性能的影响
    前言:研究了一种8090Al-Li合金平衡相T2(Al6CuLi3)和δ(AlLi)数量变化对合金室温力学性能的影响。结果表明,合金经过双级时效(210-300℃,4h+回复处理+160℃,100h)后,T2相的大量析出会使合金的强度有所降低,塑性有一定程度升高,而δ相的大量析出迅速降低合金的强度,大幅度提高塑性。
    Effects of contents of equilibrium phases T2 and δ in 8090 Al-Li alloy with composition (mass fraction, %) of Al-2.45Li-1.21Cu-1.20Mg-0.15Zr on its mechanical properties had been studied. The results show that, after double-aging treatments (210-300℃, 4h+retrogression+160℃, 100h), a large amount of precipitation of T2 may reduce the strength and improve the enlongation of the alloy to a certain extent, but a large amount of precipitation of δ may reduce the strength and improve the elongation of the alloy g...
文献名称 平衡相对8090Al-Li合金力学性能的影响
Article Name
英文(英语)翻译
EFFECTS OF EQUILIBRIUM PHASES ON MECHANICAL PROPERTIES OF 8090 Al-Li ALLOY;
作者 张万明; 张匀; 胡壮麒; 刘玉林; 赵洪恩;
Author ZHANG Wanming;ZHANG Yun;HU Zhuangqi;LIU Yulin;ZHAO Hong'en;(Institute of Metal Research;Chinese Academy of Sciences;Shenyang 110015);
作者单位
Author Agencies
中国科学院金属研究所;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 Al-Li合金; 热处理; 平衡相; 力学性能;
Keywords Al-Li alloy;heat treatment;equilibrium phase;mechanical property;
脉冲大电流扩散焊接Al-Li合金1420
Al-Li合金回归再时效的微观相场模拟
应力作用下Al-Li合金的腐蚀行为研究
Al-Li合金的研究进展
Al-Li合金分级时效的微观相场模拟
二次挤压对Al-Li合金组织及性能的影响
X射线衍射及散射方法研究Al-Li合金回火相变
合金元素对Al—Li合金组织结构和性能的影响
Zr对Al-Li合金晶粒细化作用的电子理论分析
Al-Li合金相变的热分析动力学表征

ChemYQ.com ©2005  京ICP备05016959号