文献名称:PST双相TiAl类单晶高温变形位错特征
    前言:利用透射电子显微镜研究了PST双相TiAl晶体高温变形后的位错组态。发现微孪晶变形、1/2<110]单位位错、<011]超点阵位错、1/2<112]超点阵位错均参与了变形。螺型<011]超点阵位错可在{100}面上分解,构成Kear-Wilsdorf锁。400℃,600℃变形时由1/2<112]位错分解形成的层错偶极子仍然存在,但数量减少。850℃变形时未发现层错偶极子,但这时1/2<112]刃型可动位错数量增加。原位加热观察表明,层错偶极子在650℃时完全消失。本文讨论了这些位错特征对TiAl合金韧脆转变特征的影响。
    The dislocation features in polysynthetically twinned (PST) TiAl crystal deformed at 400, 600 and 850℃ have been investgated by TEM. Screw <011] superdislocations turned to dissociate on {100} planes to form Kear-Wilsdorf locks. Faulted dipoles were found in specimens deformed below 600℃ , whereas no faulted dipole was found at 850℃.In-situ heating observations on the faulted dipoles formed during deformation at room temperature indicated that the faulted dipole disappeared at about 600℃. Based on these exp...
文献名称 PST双相TiAl类单晶高温变形位错特征
Article Name
英文(英语)翻译
DISLOCATION FEATURES IN POLYSYNTHETICALLY TWINNED TiAl CRYSTALS AFTER DEFORMATION AT HIGH TEMPERATURE;
作者 刘毅; 林栋梁; 汪德宁; 陈达; 陈世朴; 刘治国; 孟祥康;
Author LIU Yi;LIN Dongliang;WANG Dening;CHEN Da;CHEN Shipu(Shanghai Jiaotong University;Shanghai 200030;State Key Laboratory of Solid State Microstructures;Nanjing University;Nanjing 210008);LIU Zhiguo;MENG Xiangkang (Nanjing University;
作者单位
Author Agencies
上海交通大学; 南京大学;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 PST晶体; TiAl; 金属间化合物; 位错; 高温变形;
Keywords polysynthetically twinned crystal;TiAl;intermetallics;dislocation;high temperature deformation;
以细观力学法确定γ-TiAl基PST晶体宏观屈服准则
γ-TiAl基PST晶体的屈服应力及孪晶影响的细观力学研究
TiAl合金PST晶体中Ti_3Al片层取向对其蠕变性能的影响
TiAl合金PST晶体高温蠕变特性及蠕变失稳机制
Ti-48Al 合金 PST 晶体显微组织及高温压缩性能
TiAl合金PST晶体变形过程与片层界面的交互作用
TiAl合金PST晶体断裂过程原位TEM观察
Ti-48at%合金PST晶体的生长与显微组织的研究
20钢奥氏体氮碳共渗后淬火态与时效态的化合物层
四种铁基合金的M■ssbauer谱研究

ChemYQ.com ©2005  京ICP备05016959号