文献名称:惰性气体凝聚法制备纳米NiAl合金的结构及磁特性
    前言:用X射线衍射及透射电镜研究用惰性气体凝聚法制备纳米NiAl合金固体的结构结果表明,纳米NiAl合金晶体结构与常规NiAl结构一致,平均粒度为8.6nm,具有较大的晶格(显微)畸变(ε=1.2%),长程有序度有所降低。退火实验显示,当温度低于800K时晶粒不明显长大,具有较好的抗晶粒生长能力。磁共振及磁化研究表明,当NiAl合金制成纳米结构后由弱(或非)磁性转变为强磁性,这种磁性转变可能与具较大的晶格畸变及长程有序度的破坏有关。
    The structure of nanostructured NiAl(n-NiAl), synthesized by inert-gas condensation, was investigated by X-ray diffraction and TEM. The results indicated that the crystal structure of n-NiAl is same as that of conventional poly-crystalline NiAl alloy(p-NiAl); and the mean grain size of n-NiAl is 8.6 nm. However, there is severe distortion in the crystal lattice of n- NiAl(the distortion ε = 1 .2%); and the long-range ordering degree of n-NiAl is lower than that of p-NiAl. Annealing experiments showed that t...
文献名称 惰性气体凝聚法制备纳米NiAl合金的结构及磁特性
Article Name
英文(英语)翻译
STRUCTURE AND MAGNETIC CHARACTER OF NANOSTRUCTURED NiAl ALLOY SYNTHESIZED BY INERT-GAS CONDENSATION;
作者 秦晓英; 张立德; 侯碧辉; 梁任又; 纪小丽;
Author QIN Xiaoying;ZHANG Lide;HOU Bihui;LIANG Renyou;JI Xiaoli(Institute of Solid State Physics;Chinese Academy of Sciences;Hefei 230031)( University of Science and Technology;Hefei 230026 )(Structure Research Laboratory;University of Science and Techno;
作者单位
Author Agencies
中国科学院固体物理研究所; 中国科技大学; 中国科技大学结构分析开放实验室;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 纳米固体; NiAl合金; 结构; 磁性;
Keywords nanostructured solid;NiAl alloy;structure;magnetism;
纳米固体超强酸SO_4~(2-)/Fe_2O_3催化合成尼泊金酸乙酯
纳米固体超强酸TiO_2/SO_4~(2-)的制备及其催化甲苯选择性硝化
纳米固体超强酸SO_4~(2-)/ZrO_2-La_2O_3催化合成环己烯研究
纳米固体超强酸S_2O_8~(2-)/ZrO_2-Fe_2O_3-SiO_2催化合成乙酸环己酯
纳米固体超强酸SO_4~(2-)/ZnO-Fe_2O_3的制备及其催化合成苯甲酸乙酯的研究
纳米固体超强酸SO_4~(2-)/Fe_2O_3催化合成没食子酸异戊酯的研究
微米或纳米固体粒子应用在齿轮副间的摩擦学特性(英文)
磁性纳米固体酸SO_4~(2-)-TiO_2-Fe_3O_4催化剂的合成、表征及催化性能的研究
纳米固体超强酸SO_4~(2-)/Fe_2O_3催化合成没食子酸正丁酯的研究
纳米固体超强酸SO_4~(2-)/ZnO催化合成乙酸异戊酯的研究

ChemYQ.com ©2005  京ICP备05016959号