文献名称:310不锈钢在H_2S/H_2/CO_2混合气氛中的高温腐蚀
    前言:310不锈钢在0.4%H2S/H2/7%CO2的混合气氛中于600℃发生硫化腐蚀。前50h的腐蚀遵从抛物线规律,延长至250h的腐蚀其增重低于抛物线增长,这一转变对应于内层铬硫化物分散颗粒态生长成为连续层。腐蚀产物层可以分为三层:最外FeS层,中间为尖晶石结构的FeCr2S4层和最内Cr3S4层
    The corrosion of 3 10SS in gas mixture of 0.4H2S / H2 / 7%CO2 at 600℃was in the form of sulfidation. The mass gain due to corrosion obeyed parabolic rate law for the initial 50 h but subsequently lower rate was observed for long time exposure up to 250 h. Such change in kinetics corresponded to structure modification of the innermost layer of chromium sulfide from its particle distribution to a continuous layer. The scale consisted of the outermost layer of FeS, the middle layer of FeCr2S4 and the innermost...
文献名称 310不锈钢在H_2S/H_2/CO_2混合气氛中的高温腐蚀
Article Name
英文(英语)翻译
HIGH TEMPERATURE CORROSION OF 310SS IN GAS MIXTURE OF H_2S/ H_2/CO_2;
作者 李陵川; 朱日彰;
Author LI Lingchuan(Tsinghua University;Beijing 100084);ZHU Rizhang(University of Science and Technology Beijing;Beijing 100083);
作者单位
Author Agencies
清华大学; 北京科技大学;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 混合气氛腐蚀; 硫化; 310不锈钢;
Keywords corrosion;sulfidation;3 10SS;
提钒转炉烟气净化系统混合气氛腐蚀探讨
从三元混合气氛腐蚀相图到四元热腐蚀相图
预氧化对Ni_3Al合金中温塑性的影响
Fe-Nb合金在600-800℃,0.1MPa纯氧中的氧化
惰性气体凝聚法制备纳米NiAl合金的结构及磁特性
M2铸造高速钢的变质研究
SiC纤维增强的钛合金基复合材料的显微结构
自生TiC_w-AlN_p/Al复合材料中TiC_w相的形成和分布
(Sm_(1-x)Y_x)_2Fe_(17)N_y的Mossbauer谱研究
AB_5型贮氢合金P-C关系的人工神经网络研究

ChemYQ.com ©2005  京ICP备05016959号