文献名称:310奥氏体不锈钢应力腐蚀的透射电镜原位观察
    前言:用自制的恒位移加载台,在透射电镜中原位观察310奥氏体不锈钢在纯水中局部溶解前后裂尖位错组态的变化以及微裂纹的形核和扩展.结果表明,310奥氏体不锈钢在室温纯水中局部阳极溶解能促进位错发射、增殖和运动,在低应力下,纳米级微裂纹在无位错区中连续或不连续形核,由于介质的作用,纳米级微裂纹并不钝化成空洞或缺口,而是解理扩展.
    The in situ TEM observations of dislocation emission, motion and the initiation of nanocrack in 310 stainless steel in water were carried out. Using a special constant deflection device,the dislocation configuration change ahead of a loaded crack tip before and after anodic dissolution in the the deionized water and the initiation, propagation of nanometre scale stress corrosion cracks have been oberved. The results showed that SCC in thin foil specimen of 310 stainless steel can occur in water.The localize...
文献名称 310奥氏体不锈钢应力腐蚀的透射电镜原位观察
Article Name
英文(英语)翻译
IN SITU TEM OBSERVATION OF SCC IN 310 STAINLESS STEEL;
作者 黄一中; 陈奇志; 褚武扬;
Author HUANG Yizhong;CHEN Qizhi;CHU Wuyang (University of Science and Technology Beijing;Beijing 100083);
作者单位
Author Agencies
北京科技大学;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 310不锈钢; 透射电镜; 位错; 阳极溶解;
Keywords stainless steel;TEM;dislocation;anodic dissolution;
热循环对TC4钛合金组织和机械性能的影响
不锈钢在Cl~-+H_2SO_4溶液中轻载下的腐蚀磨损
急冷Cu_(30)Al_(70)合金的结构及催化特性
Fe_(73.5)Cu_(1.0)Mo_(3.0)Si_(13.5)B_(9.0
Sn-Zn钎料与Al的作用机制
磁控溅射制备Fe/Ti多层膜的结构和磁性
纤维增强金属基复合材料的应力集中及力学性能
VIRALL复合板的振动阻尼特性
原位AlN-TiC粒子增强铝基复合材料
利用Marangoni对流制备均质偏晶合金

ChemYQ.com ©2005  京ICP备05016959号