文献名称:二苯基甲烷二异氰酸酯-二乙基甲苯二胺聚脲的光谱分析和热分析
    前言:采用广角 X 射线衍射光谱法、傅里叶变换红外光谱法和示差扫描量热法,研究了由等摩尔4,4′-二苯基甲烷二异氰酸酯3,5-二乙基甲苯二胺在油浴40℃、反应2h 下制备的聚脲的结构。结果表明,聚脲可以形成结晶度为52.9%的微晶,在 FTIR 谱图的脲羰基区存在1691,1678,1657,1642cm~(-1)谱带。在结晶熔点以下对试样进行热处理,聚脲聚集态结构发生了某种不可逆的变化。
    The spectral and thermal analyses of the polyurea based on 4,4′-diphenylmethane di- isocyanate(MDI)and 3,5-diethylmethane diamine(DETDA)were carried out by WAXD,FTIR and DSC methods.The WAXD analysis showed that crystallite was formed in the polyurea.Four FTIR bands, 1691,1678,1657 and 1642 cm~(-1),were shown in the carbonyl region of the FTIR spectrum of the polyurea.A nonreversible change of the polyurea structure was observed under thermal treatment near 120℃.The bands and the change were considered to b...
文献名称 二苯基甲烷二异氰酸酯-二乙基甲苯二胺聚脲的光谱分析和热分析
Article Name
英文(英语)翻译
SPECTRAL AND THERMAL ANALYSES OF POLYUREA BASED ON MDI AND DETDA;
作者 罗宁; 王得宁; 应圣康;
Author Luo Ning Wang Dening Ying Shengkang (Institute of Material Science and Engineering;East China University of Science and Technology;Shanghai);
作者单位
Author Agencies
华东理工大学材料科学研究所; 华东理工大学材料科学研究所 上海; 200237;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 4; 4′-二苯基甲烷二异氰酸酯; 3; 5-二乙基甲苯二胺; 聚脲; 氢键; 光谱分析; 热分析;
Keywords 4;4′-diphenylmethane diisocyanate;3;5-diethylmethane diamine;polyurea;spectral analysis;thermal analysis;
用乳液聚合法制备聚苯胺/SBS导电复合材料
双环戊二烯衍生物的解二聚温度
顺酐化EPDM的合成及其对聚甲醛/顺丁橡胶的增容作用
Ni(naph)_2-(i-Bu)_(6-n)Al_2Cl_n催化丁二烯聚合
混炼胶长口型挤出胀大比的预测
氯丁橡胶同步带模塑成型工艺
阻燃耐油型船用电缆护套
反应注射成型聚氯酯/乙烯基醋树脂互穿聚合物网络的化学键效应(英文)
橡胶硫化返原动力学研究(英文)
微波作用下的甲基丙烯酸甲酯的本体聚合(英文)

ChemYQ.com ©2005  京ICP备05016959号