文献名称:碳钢在亚硫酸铵蒸煮液中腐蚀产物的表面相分析
    前言:本实验用Xk光电子能谱(XPS)和俄歇电子能谱(AES)分别对碳钢材料在不同温度亚硫酸铵制浆蒸煮液中的腐蚀产物进行了表面分析.发现在温度较高的条件下,碳钢处于钝化态时,其表面产物的外层为亚硫酸亚铁铵结晶层,内层为铁的氧化物.而在温度较低的条件下,碳钢处于活化态时,其表面产物的外层为硫化亚铁、铁的氧化物和亚硫酸亚铁铵的混合物,内层主要为硫化亚铁.
    The surface film of carbon steel immersed in neutral ammonium sulfite cooking liquor was studied.It was found that in passive conditions double layers were formed in the surface of steel,the outer layer was mostly consisted of (NH 4) 2Fe(SO 3)·H 2O crystals,the inner layer was mostly consisted of iron oxide, and in active conditions the surface film was mostly consisted of FeS.
文献名称 碳钢在亚硫酸铵蒸煮液中腐蚀产物的表面相分析
Article Name
英文(英语)翻译
Analysis of the Film on the Steel Surface Immersed in Neutral Ammonium Sulfite Cooking Liquor;
作者 杨德庆; 徐坚颖; 曲桉;
Author Yang Deqing 1 Xu Jianying 2 Qu An 2 (1: Northwest Institute of Light Industry;Xi'an;Shangxi;China;712081;2: School of Chemical Light Industrial Engineering;YPU;Kunming;650051);
作者单位
Author Agencies
西北轻工业学院; 云南工业大学;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 亚硫酸铵蒸煮液; 碳钢; 表面分析;
Keywords Surface film;Carbon steel;Ammonium sulfite cooking liquor;
硼硫、硼氮共渗组织和性能及其机理的研究
热挤压凸模结构优化设计
中压缸铸钢件缩孔(松)的计算机预测
Isolation and Fermentation of Superproteolytic Bacteria from Tropic Proteinous Fermented Food
废糖蜜制食用糖浆初探
用动态边界条件计算法模拟典型铸件凝固进程
轴对称复合挤压过程的数值模拟及实验研究
用于TCF漂白的低卡伯值纸浆的实验室研制
半水-二水湿法磷酸工艺设计方法和工业实践
丽江古城环境整治与建筑更新

ChemYQ.com ©2005  京ICP备05016959号