nature : the weld solidification formed under high temperature or crack. Most are in the seam, but also are located along the grain boundaries of austenite cracking occurs. From the form of cracks, crack formation mechanism and cracks the temperature range several aspects, such as consideration, it can heat crack into the following three : mold crack, high-temperature liquefied crack, crack multilateral.